KOTAR43 – S330

Area of Use

Ideal for desanding small sized cast iron parts, surface cleaning of steel plate and profiles, surface blending after grinding 

  • Pipe joints 
  • Oxide and scale removal from 3 – 5 mm steel plate and profiles 
  • Small size cast iron automotive parts 
  • Small size forged steel parts 
  • Toggle (shipbuilding industry), 
  • Surface preparation after machining 
  • Oxide and Scale removal of thick-walled bright steel parts.
SAE
Mesh
No
Screen Opening
mminc
KOTAR43
S330
141,400,056All pass
161,180,0475% max
181,000,039
200,850,03385% min
250,710,02896% min
350,500,02
Chemical Analysis Applications
Carbon% 0,10 -  % 0,15
Manganese% 1,20 - % 1,50
Silicon% 0,10 - % 0,25
Sulphurmax. % 0,035
Phosphorusmax. % 0,035

Hardness

TOÇELİK LOW CARBON STEEL SHOT is subject to hardness testing that requires at least 90% of the shot sample falling within the range of 43-44 HRC. 

Density

Density must be 7.0 g / cm3 minimum

Microstructure

As a result of the bainitic microstructure, TOSÇELİK LOW CARBON STEEL SHOT has a higher level of hardness and greater service life.

General Look

Steel Shot is required to be in a spherical form as much as possible. Extended or compound particles, tails, hollows, broken pieces, shrinkage, slag and dirt have to be at a minimum level.

Sectors

Steel shot is mainly used in foundries, steel mills, forging shops, rolling mills, machine shops, structural steel mills that are serving automotive, construction, ship building, aerospace, agriculture and many other industries. 

Applications

Sand Removal, Deburring, Descaling, Oxide Removal, Surface Treatment, Stress Relieving, Shot Peening